Abstract Given the environmental impacts associated with the production of conventional Portland cement, the study of special cements with reduced environmental impact has been a trend. In this context, cements containing ye'elimite (YCC) stand out due to their low CO 2 emissions. Despite the environmental advantages, the high demand for aluminum economically limits the production of these cements.An alternative to making its production feasible is using residual raw materials as a source of Al 2 O 3 , such as SFCC (spent fluidized catalytic cracking).In view of this, this work aims to evaluate hydration at the initial age of cements. For this, six clinkers were produced with different ye'elimite contents, with and without SFCC. These were characterized by XRD/Rietveld. The pastes were evaluated by TG/DTG and XRD/Rietveld to understand the hydration mechanism on the third day of these cements. It was possible to synthesize the main phases of YCC, in clinkers with and without SFCC. In addition, at the age evaluated, the pastes with and without SFCC presented comparable phase composition, indicating the potential for co-processing this residue.

Resumo Diante dos impactos ambientais associados à produção do cimento Portland convencional, o estudo de cimentos especiais de reduzido impacto ambiental tem sido uma tendência. Neste contexto, os cimentos contendo ye’elimita (YCC) se destacam devido à baixa emissão de CO2. Apesar das vantagens ambientais, a alta demanda por alumínio limita economicamente a produção destes cimentos. Uma alternativa para viabilizar a sua produção é o uso de matérias-primas residuais como fonte de Al2O3, a exemplo do SFCC (catalizador gasto do craqueamento catalítico de leito fluidizado). Diante disso, este trabalho tem como objetivo avaliar a hidratação na idade inicial de cimentos YCC produzidos a partir do coprocessamento do SFCC. Para isso, foram produzidos seis clínqueres com diferentes teores de ye’elimita, com e sem SFCC. Estes foram caracterizados por DRX/Rietveld. As pastas foram avaliadas por TG/DTG e DRX/Rietveld para compreender o mecanismo de hidratação em idade inicial destes cimentos. Foi possível sintetizar as principais fases dos YCC, nos clínqueres com e sem SFCC. Além disso, na idade avaliada, as pastas com e sem SFCC apresentaram composição de fases comparáveis indicando o potencial de coprocessamento do SFCC neste tipo de cimento.

This study evaluates the influence of milling on the reactivity of drilling cuttings (DC) utilized as supplementary cementitious material in ternary cements (TC). The drilling cuttings milling study varied the time (2, 5, 10, 15, and 20 min) and rotation speed (200 and 300 rpm), determining the specific milling energy and grindability index. The hydration of TC pastes containing DC with different particle size distributions was evaluated by isothermal calorimetry during the first 72 hours, XRD/Rietveld at 3 and 28 days, compressive strength and absorption. The incorporation of milled DC improved the TC hydration kinetics compared to reference pastes of ordinary Portland cement (REF.PC). After 28 days, the TC pastes with the D50% diameter smaller than 11 µm reached at least 70% of the resistance to the strength of the Portland cement paste. Milled DC contributes to the physical and nucleation effect of the TC pastes studied and can be used as an SCM.

Resumo Não há pesquisas que demonstrem o efeito de matérias-primas residuais combinadas como alternativa às fontes naturais em cimentos do tipo LC 3 . Nesse contexo, o objetivo deste estudo é avaliar a influência da composição de cimentos ternários contendo resíduos industriais sobre as suas propriedades reológicas e de hidratação. Como matérias-primas foram utilizados cimento Portland (CP), resíduos de bloco cerâmico (RBC), de porcelanato (RP), de mármore (RM) e fosfogesso (FG). O comportamento reológico das pastas foi analisado pela evolução do mini-abatimento no tempo e reometria rotacional. A hidratação foi avaliada por calorimetria isotérmica e DRX/Rietveld. Um incremento na área superficial específica implicou no aumento da tensão de escoamento e viscosidade plástica da pasta. O RBC e RP possuem reatividade pozolânica, apresentando incremento do teor de fases não cristalinas (incluindo C-S-H).Os CTs atingiram no mínimo 70% da resistência à compressão da pasta de CP V ARI. Os resultados sugerem que os resíduos RBC, RP, RM e FG podem ser utilizados como alternativa para redução do fator clínquer e redução dos impactos ambientais e econômicos associados à extração de matérias-primas naturais para produção de cimentos.

Abstract No research demonstrates the effect of combined waste raw materials as an alternative to natural sources in Limestone Calcined Clay Cement (LC3). In this context, this study aimed to evaluate the influence of the composition of ternary cements (TCs) containing industrial waste on their rheological and hydration properties. As raw materials, Portland cement and clay brick (CBW), clay tile (CTW), marble (MW), and phosphogypsum (PG) wastes were used. The rheological behaviour of the pastes was analysed by the mini-slump evolution over time and rotational rheometry. Hydration was evaluated by isothermal calorimetry and XRD/Rietveld. An increase in the specific surface area enhances the yield stress and plastic viscosity of the paste. CBW and CTW have pozzolanic reactivity, presenting an increase in the content of non-crystalline phases, including calcium silicate hydrate (C-S-H). The TCs reached at least 70% of the compressive strength of theHigh Early Strength Portland cement paste.The results suggest that CBW, CTW, MW and PG can be used as an alternative to reduce the clinker factor and decrease the environmental and economic impacts associated with extracting natural raw materials for cement production.

Resumo Embora a utilização de matérias-primas residuais como materiais cimentícios suplementares (MCS) seja uma temática crescente na literatura, o processo de beneficiamento por moagem e seus parâmetros ainda são pouco explorados e apresentados.Nesse contexto, o presente estudo visa avaliar os parâmetros de moagem para o beneficiamento dos resíduos de mármore, porcelanato, bloco cerâmico e fosfogesso para reciclagem como MCS. As matérias-primas foram beneficiadas por britagem, peneiramento e moagem em um moinho planetário de bolas variando os parâmetros de tempo e velocidade de rotação. Os resíduos foram caracterizados por picnometria, DSC, área superficial específica BET, FRX, TG e DRX/Rietveld. Os resíduos com composição mineralógica de fases formadas em temperaturas mais elevadas estão associados a maior demanda de energia específica de moagem e menores índices de moabilidade. O RM apresenta composição mineralógica semelhante ao do calcário comercial e o FG pode ser uma alternativa à gipsita natural em materiais cimentícios. O RBC e RP apresentam potencial de uso como MCS em substituição às argilas naturais calcinadas, embora o RP demande maior energia durante o beneficiamento por moagem.

Abstract Despitethe increasing number of publications on residual raw materials as supplementary cementitious materials (SCM), the milling beneficiation process and its parameters have been underexplored and presented. In this context, this study aims to evaluate the milling parameters for marble, clay tile, clay brick, and phosphogypsum waste processing for recycling as SCM. The raw materials were benefitted by grinding, sieving, and milling in a planetary ball mill, varying the time and rotation speed parameters. The waste was characterised by helium gas pycnometry, DSC, BET specific surface area, XRF, TGA, and XRD/Rietveld. Waste materials in which the mineral composition of phases was formed at higher temperatures were associated with higher demands for specific milling energy and lower grindability indexes. Marble waste (MW) has a mineral composition similar to commercial limestone and phosphogypsum (PG) can be an alternative to natural gypsum in cementitious materials. Clay brick waste (CBW) and clay tile waste (CTW) have the potential to be used as SCM to replace calcined natural clays, although CTW requires higher energy during milling processes.

Resumo A utilização das telas para reforço da camada de revestimento em fachadas tem se tornado uma excelente aliada na prevenção e redução de fissuras, pois podem absorver as tensões que surgem no sistema de revestimento. Esta pesquisa busca avaliar a incidência de fissuras de revestimentos reforçados com telas, submetidos à variação térmica, visando contribuir para o conhecimento do desempenho e comportamento das telas nos revestimentos argamassados. Para tanto, foi avaliada a resistência à tração direta de três telas (uma de polietileno e duas galvanizadas) a serem empregadas como reforço em argamassas analisadas quanto à resistência à compressão, tração, flexão e cisalhamento. Em seguida, foram construídos protótipos de fachadas revestidos com reboco reforçado com tela observando-se o comportamento do sistema após carregamento térmico (38 ºC e 80 ºC) por meio de termografia, mapeamento de fissuras e resistência ao impacto, avaliando-se, ainda, a eficiência de duas metodologias de reparo de fissuração (tela poliéster com massa acrílica e resina epóxi). Os resultados revelaram que a tela galvanizada eletrossoldada apresentou melhor desempenho ao absorver parte das tensões e reduzir as aberturas das fissuras, garantindo ao conjunto melhor resistência à flexão, e ambas as metodologias de reparo analisadas apresentaram desempenho adequado ante a exposição térmica.

Abstract The use of mesh for facade cladding reinforcement has become a highly effective way to help in preventing and reducing cracks, as it can absorb the stresses that occur in the coating system. This research study seeks to evaluate the incidence of cracks in mesh reinforced coatings submitted to thermal variation, aiming to contribute to the knowledge of the performance and behaviour of mesh in mortar coatings. Hence, the direct tensile strength of three different meshes (one made of polyethylene and two galvanised ones) was evaluated with regards to their use as reinforcement in mortars. The properties analysed were compression, tensile, flexion and shear strength. Thereafter, prototypes of facades coated with mortar reinforced with mesh were constructed, observing the behaviour of the system after thermal loading (38 ºC and 80 ºC) by means of thermography, crack mapping and impact resistance, further evaluating the efficiency of two crack repair methodologies (polyester mesh with acrylic plaster and epoxy resin). The results revealed that the electro-welded galvanised mesh produced a better performance, as it absorbed part of the stresses and reduced the crack openings, guaranteeing better flexural strength. Both repair methodologies showed an adequate performance with regards to thermal exposure.

RESUMO O estudo dos parâmetros reológicos das pastas cimentícias pode fornecer informações importantes sobre o desempenho dos concretos frescos nos quais elas serão aplicadas. Nesse contexto, este trabalho visa estudar os efeitos da temperatura nos parâmetros reológicos de pastas cimentícias aditivadas com superplastificantes. Também é abordada a análise do efeito do tipo de cimento, bem como o estudo da ação de superplastificantes à base de policarboxilato considerando sua função e os seus teores na mistura. As pastas foram avaliadas pelo ensaio de mini-abatimento e os parâmetros de tensão de escoamento, viscosidade plástica e indicador de tixotropia foram estimados a partir do ensaio de reometria rotacional e aplicação dos modelos de fluidos de Bingham e Herschel-Bulkley. Os resultados indicaram que o aumento da temperatura levou a uma redução das tensões de escoamento, viscosidades plásticas e tixotropia das pastas. Efeito semelhante ocorreu após o incremento do teor de aditivo até a dosagem de saturação. Para as formulações com o aglomerante de maior teor de pozolana as tensões de escoamento e viscosidades plásticas foram superiores em até 80 e 70%, respectivamente. Os dados reológicos indicam que aditivos de diferentes funções (abertura, espalhamento e multifuncional), embora apresentem a mesma base, influenciam de forma distinta os parâmetros reológicos e plasticidade das pastas cimentícias.

ABSTRACT The study of the rheological parameters of the cementitious pastes can provide important information on the performance of fresh concretes in which they will be applied. In this context, this paper aims to study the effects of temperature on the rheological parameters of cementitious pastes added with superplasticizers. It is approached the analysis of the effect of type of cement in pastes rheological behavior, as well as the study of the action of superplasticizers based on polycarboxylate considering its function and its contents in the mixture. The pastes were evaluated by the mini-slump test and the parameters of yield stress, plastic viscosity and thixotropy were estimated by the rotational rheometry test and application of Bingham and Herschel-Bulkley fluid models. The results indicated that the increase in temperature led to a reduction of the yield stresses, plastic viscosities and thixotropy of pastes. A similar effect occurred after increasing the admixture content up to the saturation content. For formulations with the binder of highest content of pozzolan, the yield stress and plastic viscosities were higher by up to 80 and 70%, respectively. The rheological data indicate that admixtures of different functions (spreading, maintenance and multifunctional), although having the same base, influence in a different way the rheological parameters and plasticity of cementitious pastes.

RESUMO O catalisador residual (CR), oriundo do Craqueamento Catalítico Fluido (FCC) em refinarias de petróleo, tem sido estudado como pozolana em materiais cimentícios para avaliação do desenvolvimento de propriedades mecânicas e durabilidade. Contudo, estudos sobre a degradação destes materiais com dióxido de carbono supercrítico (scCO2) são recentes. Este artigo avalia a degradação de pastas endurecidas com substituição da massa do cimento por CR (0%, 15% e 30% de CR) expostas durante 7 h ao scCO2, na condição de temperatura e pressão estimada para 760 m de profundidade (53,55 °C/12,41 MPa). A densidade das pastas foi fixada em 1,89 g/cm3 e tempo de cura de 28 dias. A formulação das pastas e condição supercrítica visou simular a aplicação na estrutura de um poço onshore no nordeste do Brasil, considerando que o contato com scCO2 aconteça após ao enrijecimento das pastas. A microestrutura foi avaliada por Difratometria de Raios-X (DRX) e Análises Térmicas (TG/DTG e DTA), a rigidez mensurada por dureza superficial Rockwell (HR15T) e áreas carbonatadas calculadas após aspersão da solução indicadora de pH. As pastas com CR possuíram dureza superficial reduzida e maior teor de água livre, indicando maior porosidade em relação a pastas contendo somente cimento. As reações pozolânicas do CR causaram redução parcial do teor de hidróxido de cálcio [Ca(OH)2] e formação de compostos cimentícios [C-S-H, C-A-S-H, C-A-H e Af(t)]. Após a exposição ao scCO2, as pastas com CR possuíram área/profundidade de carbonatação maiores em relação à pasta 0% CR. A formação do CaCO3 acarretou acréscimo da dureza superficial principalmente nas pastas com CR. Devido as reações com scCO2, as pastas contendo CR tiveram compostos cimentícios parcialmente descalcificados, contudo, permanecendo com teores equivalentes ou superiores aos encontrados na pasta 0% CR cuja carbonatação causou redução parcial do Ca(OH)2.

ABSTRACT The residual catalyst (CR) from Fluid Catalytic Cracking (FCC) in petroleum refineries has been studied as pozzolan in cementitious materials to evaluate the development of mechanical properties and durability. However, studies on the degradation of these materials with supercritical carbon dioxide (scCO2) are recent. This article evaluates the degradation of hardened pastes with replacement of cement mass by CR (0%, 15% and 30% CR) exposed for 7 h to scCO2, in the temperature and pressure condition estimated at 760 m depth (53,55 °C / 12,41 MPa). The density of the slurries was set at 1.89 g/cm3 and curing time of 28 days. The formulation of the slurries and supercritical condition aimed to simulate the application in the structure of an onshore well in the northeast of Brazil, considering that the contact with scCO2 happens after the hardening of the slurries. The microstructure was evaluated by X-ray diffraction (XRD) and Thermal Analysis (TG / DTG and DTA), hardness measured by Rockwell surface hardness (HR15T) and carbonated areas calculated after the pH indicator solution was sprayed. The slurries containing CR had reduced surface hardness and higher free water content, indicating a higher porosity in relation to pure cement slurries. The pozzolanic reactions of CR caused partial reduction of calcium hydroxide [Ca(OH)2] content and formation of cementitious compounds [C-S-H, C-A-S-H, C-A-H and Af(t)]. After exposure to scCO2, the pastes with CR had a larger area/depth of carbonation than the 0% CR paste. The formation of CaCO3 resulted in an increase in surface hardness mainly in the pastes with CR. Due to the reactions with scCO2, the CR-containing pastes had partially decalcified cementitious compounds but remained equivalent to or higher than those found in the 0% CR paste whose carbonatation caused a partial reduction of Ca(OH)2.

Resumo O craqueamento catalítico em leito fluidizado (FCC) é usado para melhorar a eficiência do refino de petróleo e o resíduo catalítico gerado é denominado como “catalisador de equilíbrio” (Ecat). O seu uso em matrizes cimentícias vem sendo estudado por diversos laboratórios de pesquisas internacionais, avaliando a sua influência na pozolanicidade, comportamento mecânico, formação de produtos hidratados e durabilidade. Entretanto, sua influência na reologia de pastas de cimento ainda é pouco conhecida. Neste trabalho foi avaliada a influência do Ecat no comportamento reológico de pastas de cimento utilizando teores de substituição do cimento pelo resíduo em 10%, 20%, 30% e 40% em massa. Foram avaliados o tempo de pega e o comportamento reológico ao longo do tempo por meio dos ensaios de mesa de consistência, squeezeflow e reometria rotacional. Os resultados mostraram que o uso do Ecat influenciou no tempo de pega e no comportamento reológico das pastas estudadas. O módulo de fluidez proposto para o ensaio de squeezeflow se mostrou eficiente na análise do comportamento reológico das pastas estudadas.

Abstract Fluid bed catalytic cracking (FCC) is used to improve the efficiency of petroleum refining and the exhausted catalyst is referred to as "equilibrium catalyst", Ecat. The use of this catalytic residue in cementitious matrices has been studied by various international research laboratories, seeking to assess its influence on pozzolanicity, mechanical behavior, formation of hydrated products and durability. However, the influence of Ecat replacements on the Rheological behavior of cement pastes is not yet fully understood. Hence, this study evaluated the rheological properties of cement pastes with 10%, 20%, 30% and 40% by weight cement replacements. Setting time and time-dependent rheological behavior were investigated using consistency tests, squeeze flow and rotational rheometry. The results showed that the use of Ecat influenced the setting time and the rheological behavior of the pastes. The flow module proposed for the squeeze flow test was effective in analyzing the rheological behavior of the studied pastes.

The influence of NaCl salt in the hydration of the Portland cement paste class G was studied using a Non Conventional Differential Thermal Analysis (NCDTA) on the first 24 hours of cement hydration. The mass of salt used corresponds to 0, 5, 10, 15 and 20% of mass of water used in the preparation of the pastes. The water/cement ratio (w/c) remained constant, being 0.46, and the pastes final volume was 99.9mL. Applying a deconvolution method to separate overlapped NCDTA peaks it was possible to estimate the energy released during the different stages of hydration and the effect of salt in cement hydration process. The presence of up to 10% of salt accelerated the hydration process and increased the hydration of C3S and C3A, while the 20% of the salt causes a delayed hydration and decreased the hydration of C3S and C3A. Futhermore, cement pastes with the same percentages of NaCl and with different hydration times were evaluated by Thermogravimetry (TG), Derivative Thermogravimetry (DTG) and Differential Thermal Analysis (DTA). After 28 days the presence of salt caused a greater increase in the formation of hydrated products.

Resumo Questões relacionadas ao meio ambiente e sua relação com o homem têm incentivado discussões e ações voltadas à prevenção dos efeitos negativos sob o meio ambiente. Para ter programas efetivos que incentivem ações mais sustentáveis na Construção Civil, é preciso saber o que as pessoas pensam e sabem sobre sustentabilidade, os significados e ideias socialmente compartilhadas. Esta pesquisa foi desenvolvida dentro de uma abordagem interdisciplinar, envolvendo a Psicologia Social e a Engenharia Civil, e tem por objetivo identificar as representações sociais de estudantes universitários dos cursos de engenharia civil e arquitetura e de ciências humanas sobre a sustentabilidade. Trata-se de um estudo descritivo, que utilizou um questionário eletrônico e o EVOC para análise dos dados. Os resultados apontaram para uma representação social da sustentabilidade associada à dimensão ambiental: ambiente, meio e natureza. As outras duas dimensões do tripé da sustentabilidade, a econômica e a social, apareceram superficialmente como representações periféricas.

Abstract Environment issues and their relationship with man have encouraged discussions and actions to prevent negative effects on the environment. To have effective programs that encourage more sustainable actions in Construction, it is necessary to know what people think and know about sustainability, the meanings and socially shared ideas. This research was developed within an interdisciplinary approach involving social psychology and civil engineering and aims to identify the social representations of college students of engineering and humanities on sustainability. It is a descriptive study that used an electronic questionnaire and EVOC for data analysis. The results point to a social representation of sustainability associated with the environmental dimension: environment, environmental, and nature. The other two dimensions of the triple bottom line, economic and social, appear superficially as peripheral representations.

Resumen Cuestiones relacionadas con el medio ambiente y su relación con el hombre han alentado debates y acciones para prevenir los efectos negativos sobre el medio ambiente. Para desarrollar programas efectivos que promuevan acciones más sostenibles en la construcción se necesita saber lo que la gente piensa y saber acerca de la sostenibilidad, los significados y las ideas socialmente compartidas. Estudio interdisciplinar que envuelve la psicología social y la ingeniería civil, y tiene como objetivo identificar las representaciones sociales de los estudiantes universitarios de ingenierías y humanidades sobre la sostenibilidad. Estudio descriptivo, que utilizó un cuestionario electrónico, y el EVOC para el análisis de datos. Los resultados apuntan para la existencia de una representación social de la sostenibilidad asociada a la dimensión ambiental: medio ambiente y naturaleza. Las otras dos dimensiones del trípode de la sostenibilidad, la económica y la social, aparecen superficialmente como representaciones periféricas.

Resumo Este artigo tem como objetivo apresentar o processo de identificação, mensuração e caracterização das perdas por transporte nos fluxos físicos de processos construtivos, considerando suas incidências, tempos, causas e consequências. A abordagem metodológica adotada foi Design Science Research, desenvolvida a partir de dois estudos de caso em processos ainda poucos empregados no Brasil, quais sejam, revestimento com argamassa projetada e Light Steel Frame. Esses estudos foram conduzidos a partir das etapas de identificação dos fluxos físicos, identificação da distribuição dos tempos dos trabalhadores e caracterização das perdas por transporte. Múltiplas fontes de evidências, ferramentas e técnicas foram utilizadas para a organização dos eventos de perda por transporte, associados a suas causas e consequências. Os resultados obtidos indicaram que a maior parte das perdas por transporte foram ocasionadas por problemas de mobilidade dentro do canteiro. Problemas causados pela falta de equipamentos apropriados foram os que mais perda de tempo ocasionaram. A redução das condições de segurança e a necessidade de um novo transporte foram as principais consequências observadas. As principais contribuições deste estudo estão relacionadas ao maior entendimento da natureza das perdas por transporte, à adoção de ferramentas e indicadores para a caracterização das perdas por transporte do ponto de vista de sua incidência e tempos, bem como uma proposta de classificação das principais causas e consequências para a caracterização dessas perdas.

Abstract This paper aims to present the process of identification, measurement and characterization of transport wastes in construction processes, taking into consideration their incidence, times, causes and consequences. The method adopted was Design Science Research, carried out through two case studies in processes that are still sparsely used in Brazil, i.e., the projected mortar coating system and the Light Steel Frame technology. The studies were conducted through the following steps: identification of physical flows, identification of the distribution of workforce production time, and identification and quantification of transport wastes' causes. Multiples sources of evidence, tools and techniques were used for the data collection in order to describe each transportation waste event, asociated on its cause and impacts. The findings indicated that most of the transport waste events were caused by problems related to access and mobility on the jobsite, however, the problems caused by lack of appropriate equipment to carry out the transport activities were the most common cause of lost time. Unsafe conditions and new transport were the principal consequences observed. The main contributions of this study are related to an improved understanding of the nature of the transportation wastes, as well as the definition of a set of tools and indicators to characterize transport waste, and a proposal of classification of transport waste causes and consequences to characterize these wastes.

Os diferentes tratamentos dados aos agregados reciclados influenciam nas propriedades das argamassas nos estados fresco e endurecido. Como esses agregados possuem características diferentes das dos agregados naturais, tais como elevada absorção, forma lamelar, textura áspera e menor massa específica, há necessidade de estudar os diferentes procedimentos empregados na dosagem de misturas contendo esses resíduos e a influência deles no comportamento físico e mecânico das argamassas. Dois procedimentos foram utilizados no presente estudo: compensação de parte da água absorvida pelos agregados miúdos reciclados (AMR), fazendo-se sua pré-saturação, e uso dos agregados secos em estufa. Este trabalho tem como objetivo principal avaliar a influência desses procedimentos de dosagem nas propriedades reológicas, teor de água quimicamente combinada e resistência à compressão de argamassas contendo 25% e 50% de agregados reciclados em substituição (em massa) aos agregados naturais. Os resultados mostram que a pré-saturação influencia as propriedades das argamassas no estado fresco e endurecido. A presença do AMR promove misturas com maior viscosidade, maior teor de água livre e menor resistência à compressão.

The different treatments given to recycled aggregates influence the properties of mortars in fresh and hardened states. As these aggregates have characteristics different from those of natural aggregates, such as high absorption, lamellar form, rough texture and lower density, there is a need to study the different procedures used in the dosage of mixtures containing these residues and their influence on the physical and mechanical behavior of mortars. Two procedures were used in this study: partial compensation of the water absorbed by the recycled fine aggregates (RFA) through their pre-saturation and use of aggregates dried in an oven. The main aim of this study is to evaluate the influence of these dosage procedures on the viscosity, chemically combined water content and compressive strength of mortars containing 25% and 50% of recycled aggregates replacing (by mass) natural aggregates. The results showed that the pre-saturation procedure influences the properties of the mortars in the fresh and hardened states. The presence of the RFA promotes mixtures with higher viscosity, higher content of free water and less resistance to compression.

Nesse trabalho, são apresentados os resultados do estudo sobre a utilização da escória de cobre como agregado miúdo para concreto. Foi avaliada a influência da utilização de diferentes teores de escória de cobre granulada, como agregado miúdo, nas propriedades mecânicas (resistência à compressão e tração) do concreto. Os resultados mostram que a utilização de escória de cobre como agregado miúdo, até 40% de substituição em volume, promove um incremento no desempenho mecânico do concreto, demonstrando a possibilidade de utilização em substituição parcial do agregado miúdo natural.

This work presents the results of the study about the use of copper slag as fine aggregate for concrete. The influence of the use of different percentages of granulated copper slag, as fine aggregate, in the mechanical properties (compression strength and splitting tensile strength) of the concrete was evaluated. The results show that the use of copper slag as fine aggregate, up to 40% of substitution in volume, promotes an increment in the mechanical performance of the concrete. The work shows the possibility of using copper slag in partial substitution of the natural aggregate.

Nesse trabalho, são apresentados os resultados do estudo da utilização do resíduo da indústria cerâmica (tijolos de argila calcinada) como material pozolânico suplementar para produção de concretos. O resíduo da indústria cerâmica foi caracterizado física, química e mineralogicamente. A viabilidade técnica da substituição do cimento por resíduo da indústria cerâmica foi avaliada. As propriedades estudadas foram o comportamento tensão versus deformação, resistência à compressão, resistência à tração na flexão e por compressão diametral. Os resultados demonstram que a substituição de cimento por 20% de resíduo cerâmico (em massa) não influenciou significativamente nas resistências à compressão e tração e promoveu concretos com maior capacidade de deformação.

This paper presents the results of a study on the use of ground calcined-clay brick residuals, produced by the ceramic industry, as a supplementary pozzuolanic cementing material for use in concrete. The ceramic residue was characterized by physical, chemical and mineralogical tests. The feasibility of the substitution of the cement by the ceramic residue was evaluated by performing mechanical tests on the concrete samples. The properties investiged were stress-strain behavior, compressive strength, flexural strength and splitting tensile strength. The results pointed out that there is a potential for the use of ceramic residue as a supplementary cementing material in concrete production. Concretes containing ceramic residue (20% of cement replacement by weight) presented equal strength and lower elastic modulus than the control mixes.